医疗级PEI, 药物,玻璃纤维增强材料10%

 

ULTEM™ Resin 2100R - Europe

聚醚酰亚胺

SABIC

Technical Data

 

Product Description

10% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.

 

General

Material Status • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 • SABIC

• ULTEM™ Resin

Availability • 欧洲

Filler / Reinforcement • 玻璃纤维增强材料, 10% Filler by Weight

Additive • 脱模

Uses • 药物

RoHS Compliance • RoHS 合规

Processing Method • 注射成型

Also Available In • Asia Pacific • Latin America • North America

Physical 额定值(英制) 额定值(公制) 测试方法

Density 1.34g/cm³ 1.34g/cm³ ISO 1183

Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) 0.549in³/10min 9.00cm³/10min ISO 1133

Molding Shrinkage - 流动 3 4.0E-3 到 6.0E-3in/in 0.40 到 0.60% Internal Method

Water Absorption ISO 62

饱和, 73°F (23°C) 1.0% 1.0%

平衡, 73°F (23°C), 50% RH 0.60% 0.60%

Mechanical 额定值(英制) 额定值(公制) 测试方法

Tensile Modulus 653000psi 4500MPa ISO 527-2/1

Tensile Stress (断裂) 16700psi 115MPa ISO 527-2/5

Tensile Strain (断裂) 4.0% 4.0% ISO 527-2/5

Flexural Modulus 4 653000psi 4500MPa ISO 178

Flexural Stress 4, 5 26800psi 185MPa ISO 178

Taber Abrasion Resistance Internal Method

1000 Cycles, 1000 g, CS-17 转轮 15.0mg 15.0mg

Impact 额定值(英制) 额定值(公制) 测试方法

Charpy Notched Impact Strength (73°F (23°C)) 3.3ft•lb/in² 7.0kJ/m² ISO 179/2C

Unnotched Izod Impact Strength 6 ISO 180/1U

-22°F (-30°C) 14ft•lb/in² 30kJ/m²

73°F (23°C) 14ft•lb/in² 30kJ/m²

Hardness 额定值(英制) 额定值(公制) 测试方法

Ball Indentation Hardness (H 358/30) 20300psi 140MPa ISO 2039-1

Thermal 额定值(英制) 额定值(公制) 测试方法

Heat Deflection Temperature 7

66 psi (0.45 MPa), 未退火, 0.157 in (4.00 410°F 210°C ISO 75-2/Be

mm), 3.94 in (100 mm) Span

264 psi (1.8 MPa), 未退火, 0.157 in (4.00 401°F 205°C ISO 75-2/Ae

mm), 3.94 in (100 mm) Span

Vicat Softening Temperature

-- 433°F 223°C ISO 306/A50

-- 414°F 212°C ISO 306/B50

-- 423°F 217°C ISO 306/B120

Ball Pressure Test IEC 60695-10-2

253 到 261°F (123 到 127°C) 通过 通过

 

ULTEM™ Resin 2100R - Europe

聚醚酰亚胺

 

SABIC

Thermal 额定值(英制) 额定值(公制) 测试方法

CLTE ISO 11359-2

流动 : 73 到 302°F (23 到 150°C) 1.4E-5in/in/°F 2.6E-5cm/cm/°C

横向 : 73 到 302°F (23 到 150°C) 3.3E-5in/in/°F 6.0E-5cm/cm/°C

Thermal Conductivity 1.7Btu•in/hr/ft²/°F 0.24W/m/K ISO 8302

RTI Elec 338°F 170°C UL 746

RTI Imp 338°F 170°C UL 746

RTI Str 338°F 170°C UL 746

Electrical 额定值(英制) 额定值(公制) 测试方法

Surface Resistivity > 1.0E+15ohms > 1.0E+15ohms IEC 60093

Volume Resistivity 1.0E+15ohms•cm 1.0E+15ohms•cm IEC 60093

Electric Strength IEC 60243-1

0.0315 in (0.800 mm), 在油中 860V/mil 34kV/mm

0.0630 in (1.60 mm), 在油中 690V/mil 27kV/mm

0.126 in (3.20 mm), 在油中 380V/mil 15kV/mm

Relative Permittivity IEC 60250

50 Hz 3.00 3.00

60 Hz 3.00 3.00

1 MHz 2.90 2.90

Dissipation Factor IEC 60250

50 Hz 9.0E-4 9.0E-4

60 Hz 9.0E-4 9.0E-4

1 MHz 2.5E-3 2.5E-3

2.45 GHz 4.6E-3 4.6E-3

Comparative Tracking Index IEC 60112

-- 150V 150V

解决方案 B 100V 100V

Flammability 额定值(英制) 额定值(公制) 测试方法

Flame Rating UL 94

0.016 in (0.41 mm) V-0 V-0

0.07 in (1.9 mm) 5VA 5VA

Glow Wire Flammability Index IEC 60695-2-12

0.13 in (3.2 mm) 1760°F 960°C

Oxygen Index 46% 46% ISO 4589-2

Injection 额定值(英制) 额定值(公制)

Drying Temperature 302°F 150°C

Drying Time 4.0 到 6.0hr 4.0 到 6.0hr

Suggested Max Moisture 0.020% 0.020%

Hopper Temperature 176 到 248°F 80 到 120°C

Rear Temperature 644 到 743°F 340 到 395°C

Middle Temperature 662 到 761°F 350 到 405°C

Front Temperature 680 到 779°F 360 到 415°C

Nozzle Temperature 662 到 761°F 350 到 405°C

Processing (Melt) Temp 698 到 770°F 370 到 410°C

Mold Temperature 284 到 356°F 140 到 180°C

 

 

 

 

 

医疗级PEI原料,医疗级聚醚酰亚胺塑胶原料， 医疗级PEI ULTEM™ Resin 2100R - Europe是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，COA原料出厂报告,REACH报告,SVHC报告,UL黄卡,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123   13549213581 肖生    QQ：15397858   微信：13549213581